Habka nadiifinta tellurium-ka 7N wuxuu isku daraa teknoolojiyada sifeynta aagga iyo jihaynta crystallization. Faahfaahinta habka muhiimka ah iyo xuduudaha ayaa hoos lagu sharraxay:
1. Geedi socodka Sifeynta Aagga
Naqshadeynta Qalabka
Doonyaha dhalaalinta aagagga lakabka badan leh: Dhexroorka 300–500 mm, dhererka 50–80 mm, oo laga sameeyay quartz ama graphite saafi ah oo sarreeya.
Nidaamka kuleylinta: Gariiradaha iska caabbinta nus-wareegsan oo leh saxnaanta xakamaynta heerkulka oo ah ±0.5°C iyo heerkulka ugu badan ee hawlgalka oo ah 850°C.
Halbeegyada Muhiimka ah
Vacuum: ≤1×10⁻³ Pa oo dhan si looga hortago oksaydheynta iyo wasakhowga.
Xawaaraha safarka aagga: 2–5 mm/saacaddii (wareejin hal dhinac ah iyada oo loo marayo usha wadista).
Heerkulka heerka: 725±5°C dhinaca hore ee aagga dhalaalay, qaboojinta ilaa <500°C geeska dambe.
Baasaska: 10–15 wareeg; waxtarka ka saarista >99.9% ee wasakhda leh isku-dhafka kala-soocidda <0.1 (tusaale ahaan, Cu, Pb).
2. Habka Kireynta Jihada
Diyaarinta Dhalaalka
Alaabta: 5N tellurium oo la nadiifiyey iyada oo loo marayo sifeynta aagga.
Xaaladaha dhalaalka: Waxaa lagu dhalaaliyaa gaaska Ar ee aan firfircoonayn (≥99.999% daahirnimo) heerkul ah 500–520°C iyadoo la isticmaalayo kuleylin soo noqnoqota oo heer sare ah.
Ilaalinta dhalaalka: Daboolka garaafka saafiga ah si loo xakameeyo isbeddelka; qoto dheer oo barkadda dhalaalaysa lagu hayo 80-120 mm.
Xakamaynta Kiristaalinta
Heerka koritaanka: 1–3 mm/saacaddii oo leh heerkul toosan oo ah 30–50°C/cm.
Nidaamka qaboojinta: Saldhig naxaas ah oo biyo lagu qaboojiyey si loogu qaboojiyo qaybta hoose ee qasabka ah; qaboojinta shucaaca ee xagga sare.
Kala soocidda wasakhda: Fe, Ni, iyo wasakhda kale ayaa lagu kobciyaa xuduudaha hadhuudhka ka dib 3-5 wareeg oo dib u dhalaalin ah, taasoo yareynaysa heerka ppb.
3. Halbeegyada Xakamaynta Tayada
Tixraaca Qiimaha Heerka Caadiga ah ee Halbeegga
Nadiifnimo kama dambays ah ≥99.99999% (7N)
Wadarta wasakhda birta ah ≤0.1 ppm
Tirada oksijiinta ≤5 ppm
Kala leexashada jihada kiristaalka ≤2°
Iska caabin (300 K) 0.1–0.3 Ω·cm
Faa'iidooyinka Habka
Scalability: Doomaha dhalaala ee aagga dahaarka badan leh waxay kordhiyaan awoodda dufcadda 3–5× marka loo eego naqshadaha caadiga ah.
Hufnaan: Xakamaynta saxda ah ee faakuumka iyo kulaylka waxay suurtogal ka dhigaysaa heerarka sare ee ka saarista wasakhda.
Tayada kiristaalka: Heerarka koritaanka aadka u gaabiska ah (<3 mm/saacaddii) waxay hubiyaan cufnaanta kala-baxa oo hooseysa iyo hufnaanta hal-kiristaalka ah.
Tellurium-kan la safeeyey ee 7N wuxuu muhiim u yahay codsiyada horumarsan, oo ay ku jiraan dareemayaasha infrared-ka, unugyada qorraxda ee khafiifka ah ee CdTe, iyo substrates-ka semiconductor-ka.
Tixraacyo:
waxay tilmaamaysaa xogta tijaabada ah ee laga helay daraasado dib loo eegay oo ku saabsan nadiifinta tellurium.
Waqtiga boostada: Maarso-24-2025